The manufacturer of FLAT TEMPERED GLASS tells you that because glass is transparent and reflective, and easy to color, it is often used in occasions that have certain requirements for light and color, such as optical instruments and various artistic decorations. Modern technology has brought new vitality and energy to the glass industry, and at the same time has greatly improved the performance of the glass. We will briefly introduce why the FLAT TEMPERED GLASS is wavy after it is released, and explain the cause and solution of this problem.

Reasons for FLAT TEMPERED GLASS:
It is because of the tempering of the horizontal rod type tempering furnace, there will be a certain interval between each ceramic rod. When the glass is burned to the softening point temperature (about 620-650 degrees), the FLAT TEMPERED GLASS will be affected by its own weight. The reason is a slight wavy deformation.
1.The glass is thin, it is easy to deform under 5mm thickness, and it is not easy to deform over 8 centimeters.
2. The ceramic rods of the tempering furnace are widely spaced, and they are prone to wavy deformation.
3. The FLAT TEMPERED GLASS manufacturer tells you that in terms of glass structure, if the glass is processed with holes or grooves, the main control should increase the temperature appropriately, otherwise it will be easy to fry, and it will also be easy to produce wave deformation.
The above is the reason of FLAT TEMPERED GLASS, I hope it will help you.